Figure 2.4 Schematic diagrams of the fabrication route of composite phase change microcapsules with paraffin core and (a) PMMA/BN/TiO2 hybrid shell.
Source: Sun and Xiao [36]. Reproduced with the permission from the American Chemical Society
or (b) MF/GO hybrid shell.
Source: Zhang et al. [37]. Reproduced with the permission from Elsevier Ltd.
2.2.2 Physical Blending
It is quite appealing that supporting materials are directly introduced into the phase change matrices via physical blending to produce shape‐stabilized phase change composites. Compounding organic PCMs, especially PW, with robust or flexible polymers featuring high melting temperature or network structure is an effective strategy to achieve this goal. Accordingly, a facile melt blending has been conducted to fabricate polymeric phase change composites, including polyethylene (PE)/PW,[39] ethylene propylene diene monomer (EPDM)/PW,[40] styrene‐b‐(ethylene‐co‐butylene)‐b‐styrene (SEBS)/PW,[41] olefin block copolymer (OBC)/PW,[42] OBC/hexadecane,[43] epoxy/PW,[44] polyolefin elastomer (POE)/lauric acid,[45] POE/stearic acid,[46] PMMA/stearic acid,[47] etc. For example, Chen et al.[48] introduced high‐density PE (HDPE), low‐density PE (LDPE), and linear LDPE (LLDPE) into PW through melt blending to fabricate three kinds of polymeric PCMs. The results indicated that the leakage behavior could be controlled by the co‐continuous structure, and the PE phase had a minor influence on the crystallinity structure and thermal transition temperatures of PW phase. For these polymeric PCMs, the organic PCMs content is maintained in the range of 30–60 wt%, and most of them can be used as shape memory devices. To impart high thermal conductivity to these polymeric PCMs, functional fillers can be added to prepare thermally conductive polymeric phase change composites,[49, 50] and more discussion will be provided in the next section.
Figure 2.5 Microstructures of (a) EVM.
Source: Deng et al. [51].
(b) EP.
Source: Zhang et al. [52].
(c) diatomite.
Source: Qian et al. [53].
(d) EG.
Source: Wang et al. [54].
(e) graphene.
Source: Shi et al. [18].
and (f) GO.
Source: Yang et al. [55].
The innovations of nanotechnology open up new frontiers in energy conversion and storage materials and systems, and thus multifarious functional nanomaterials can act as supporting materials to prepare shape‐stabilized polymeric phase change composites. Effective supporting nanomaterials shown in Figure 2.5 possess the following three main characteristics:
1 Micro/nanoporous structure can provide capillary force to accommodate PCMs. Typical candidates include expanded vermiculite (EVM),[51] expanded perlite (EP),[52] diatomite,[53] expanded graphite (EG),[54] and activated carbon[56].
2 Large specific surface area can yield strong surface tension to absorb PCMs. The typical representatives are two‐dimensional (2D) graphene with a specific surface area of 2630 m2 g−1[57] and MXene[58].
3 Hydrogen bonding interaction can restrict the molecular chain motion of PCMs. Typical materials are SiO2,[59] GO,[14] and cellulose[60]. There are strong hydrogen bonding interactions between these materials and PEG with oxygen‐containing functional groups. A typical example is the PEG‐based shape‐stabilized composites with ultra‐low content of GO (4 wt%).[14]
2.2.3 Porous Supporting Scaffolds
Considering the complicated technological process of micro/nanoencapsulated PCMs and the low utilization efficiency of functional materials in the processing of phase change composites through physical blending, impregnating PCMs into porous supporting scaffolds to develop form‐stable PCMs with high energy storage density has attracted extensive attention in recent years. Lightweight three‐dimensional (3D) porous supporting architectures not only inherit the intrinsic characteristics from individually functional components but also create new collective properties from the monoliths, including large specific surface area, high porosity, and unique network structure, and these features are beneficial to improving the comprehensive performance of PCMs through the strong interactions between PCMs and supporting components in the form of hydrogen bonding, interfacial adhesion, capillary force, and van der Waals forces. Therefore, their physicochemical characteristics, such as pore size, specific surface area, and hydrophilicity or hydrophobicity, have an important influence on the properties of the final composites. The porous supporting scaffolds for polymeric phase change composites can be divided into three categories: polymeric porous scaffolds, inorganic porous scaffolds, and organic–inorganic hybrid porous scaffolds.
Polymeric porous scaffolds with high strength/weight ratio and porosity, such as poly(vinyl alcohol) (PVA) aerogel,[61] PU foam,[62] and polypropylene (PP) aerogel,[63] have been acted as excellent supporting materials for PCMs. More interestingly, a rapid preparation of PEG‐based phase change composites containing 3D cellulose network constructed by UV‐induced thiol‐ene click chemistry has been achieved by a solvent exchange strategy without additional freeze‐drying operation.[64] In comparison to polymeric porous scaffolds, inorganic porous scaffolds can provide supporting effect and conductive network simultaneously. The above‐mentioned partial supporting nanomaterials can be constructed into 3D porous scaffolds (e.g. biological porous carbon,[16] GO aerogel,[65] GO/BN scaffolds,[66] and hybrid graphene aerogels[55]) by high‐temperature pyrolysis (biomass carbonization), self‐assembly, and other methods, and then they can be introduced into phase change matrices to effectively prepare shape‐stabilized polymeric phase change composites. Additionally, it is difficult for a portion of functional fillers to form 3D structural materials by themselves, and organic components are often required as additives. The most popular one is cellulose‐based composite scaffolds, successfully developing cellulose/CNT,[67] cellulose/graphene nanoplatelets СКАЧАТЬ