High-Performance Materials from Bio-based Feedstocks. Группа авторов

Чтение книги онлайн.

3 Starbon^®: Novel Template‐Free Mesoporous Carbonaceous Materials from Biomass – Synthesis, Functionalisation and Applications in Adsorption, and Catalysis

       Duncan J. Macquarrie, Tabitha H.M. Petchey and Cinthia J. Meña Duran

       Green Chemistry Centre of Excellence, Department of Chemistry, University of York, York, UK

3.1 Introduction

      Porous materials are of great importance in a wide range of applications, including adsorption, catalysis, energy applications and composite materials. The majority of these materials are microporous; from the International Union of Pure and Applied Chemistry(IUPAC) definition [1, 2] they contain pores of <2 nm. In reality, the pores are generally constrained to <1 nm, making them able to adsorb small molecules within their pore structure, whereas larger molecules can only adsorb externally, meaning that the majority of the surface area is unavailable. Long micropores also suffer from diffusional issues, and it is recognised that much of a pore system may indeed play little role in the material’s performance.

These issues have driven research into the development of mesoporous materials (IUPAC definition encompasses pores from 2 to 50 nm) which allow much faster diffusion and thus utilise a greater proportion of the pore system. These larger pores are generally less easily blocked than the much smaller micropores, but a proportion may have constrictions such as the classic ‘ink bottle’ shape with a narrow entrance to a much larger space. It is very much possible that the mesoporous materials also contain micropores, and the mesopores may play a role in improving access to the micropores.

      While (amorphous unstructured) mesoporous materials such as silica and alumina have been known for decades, more regular materials took much longer to develop. It was the early 1990s that saw an explosion of methodologies that delivered a wide range of very controllable routes to highly regular structured materials, largely silicas, but also a few alumina systems and others were developed [3, 4]. This work served to illustrate the advantages of mesoporosity, with a range of applications being demonstrated.

      While these strides were being made in inorganic materials, the field of carbon was still dominated by predominantly microporous activated carbons, generally prepared in two steps. The first step is the thermal decomposition of waste biomass, which is followed by a chemical ‘activation’ step. This second step usually involved reaction with metal species (KOH and ZnCl₂ in large quantities) or gases (oxidants such as oxygen or CO₂) in order to open up the structure and generate some mesoporosity. Nonetheless, these materials remain predominantly microporous.

      The enormous activity in well‐defined, highly mesoporous inorganic materials led to their use as templates, including for carbon, and various groups have published work showing that the mesopores could be filled with organic material which could then be carbonised [5, 6]. Removal of the inorganic template then gave an inverse replica carbonaceous material that often displayed mesoporosity.

      These so‐called hard templating methods provide a wide range of well‐ordered materials [7] but have the drawback of complex and wasteful syntheses, destroying both the template for the silica and the silica itself. An elegant approach has recently been put forward by Jiang et al. [8] who coated the internal surface of mesoporous silicas with a layer of carbon, leading to carbon silica composites (CSCs). Such CSCs directly replicate the porosity of the silica but have a carbonaceous surface. This route is simpler, less wasteful, and retains positive features from the silica, including mechanical strength and the variety of pore architectures that silica can have.

      Another approach, first published in 2006, utilises the inherent structure of certain polysaccharides to expand to give mesostructured hydrogels [9]. With suitable drying strategies, these gels can be dried and the resultant aerogel is pyrolysed to provide a highly mesoporous material with excellent pore volume, surface area, and importantly, tunable surface properties ranging from polysaccharide‐like at lower pyrolysis temperatures to carbon‐like at higher temperatures. While the process consists of three stages, it does not involve templating, instead relying on the inherent properties of the starch to assemble into naturally mesoporous structures. These materials are known as Starbon^®, from a combination of starch and carbon, and will be the focus of this chapter. Starbon has been commercialised by Starbons СКАЧАТЬ