The Rheology Handbook. Thomas Mezger
Чтение книги онлайн.
Читать онлайн книгу The Rheology Handbook - Thomas Mezger страница 16
Название: The Rheology Handbook
Автор: Thomas Mezger
Издательство: Readbox publishing GmbH
Жанр: Химия
isbn: 9783866305366
isbn:
Example 2: Suggestions for test profile presets, with γ ̇ (t) as a ramp function
1) Linear preset
Preset: γ ̇ = 0 to 1000 s-1 with 20 measuring points in a period of t = 120 s for the total test interval. The shear rates are increased in steps showing always the same distance between their values when presenting the curves on a linear scale (they are therefore equidistant; see Figure 3.1). In this case, each one of the measuring points is generated by the rheometer in the same period of time. In this example, the test program results in a duration of t = 6 s for each single measuring point.
2) Logarithmic preset
Preset: γ ̇ = 0.01 to 1000 s-1 with 25 measuring points. The shear rates are increased in logarithmic steps, now showing the same distance in between neighboring points, but of course, only when using a logarithmic scale. Here, a variable logarithmic measuring point duration should be preset, for example, beginning with t = 100 s and ending with t = 5 s. Therefore, when using this method, longer measuring point durations are occurring at lower shear rates, and shorter durations at the higher ones. As a consequence, for each single measuring point in the low-shear range the transient effects of the sample will be either reduced to a minimum or they have already completely decayed at the end of the prolonged duration of each measuring point.
Figure 3.5: Viscosity functions of a dispersion, occurrence of time-dependent effects in the low-shear range such as the “transient viscosity peak”, when presetting too short measuring point duration: (1) clearly too short; (2) better, but still too short; (3) sufficiently long
Example 3: Occurrence of a “transient viscosity peak” when presetting a too short measuring point duration in the low-shear range (e. g. when testing dispersions and gels)
Figure 3.5 presents three viscosity functions of the same dispersion all curves are measured in the range between γ ̇ = 0.01 and 100 s-1.
Preset for the duration of each individual measuring point:
Test 1: t = 10 s = const (i. e., with the same time for each one of the measuring points),
Test 2: t = 60 to 5 s (i. e., with variable time, decreasing towards higher shear rates),
Test 3: t = 120 to 5 s (similar to Test 2, but beginning with a longer time)
Results: Dispersions and gels when showing stability at rest, thus, a gel-like viscoelastic structure, usually display a constantly falling η-curve from low to high shear rates, at least in the low-shear range (i. e. at γ ̇ < 1 s-1). This behavior is indicated by the curve of Test 3. In contrast, the η-curves of Tests 1 and 2 are showing “transient viscosity peaks”, since here, still time-dependent effects are measured. The shorter the selected measuring point duration in the low-shear range, the lower are the η-values determined in this range, and the higher are the shear rate values at the occurrence of the peaks.
Summary: When testing dispersions and gels
The longer the measuring point duration in the low-shear range, the greater is the chance to avoid transient effects.
Note: Uncrosslinked polymers in the form of solutions and melts usually show a constant
η-value in the low-shear range, which is the plateau value of the zero-shear viscosity η0 (see Chapter 3.3.2.1a, Figure 3.10). However, also here a “transient viscosity peak” might appear when presetting too short measuring point durations in this shear rate range.
Figure 3.6: Flow curve of a shear-thinning liquid
Figure 3.7: Viscosity curve of a shear-thinning liquid
3.3.2Shear-thinning flow behavior
Viscosity of a shear-thinning material depends on the degree of the shear load (shear rate or shear stress, respectively). The flow curve shows a decreasing curve slope (see Figure 3.6), i. e., viscosity decreases with increasing load (see Figure 3.7).
Examples of shear-thinning materials
Polymer solutions, polymer melts, organic binders (e. g. methylcellulose), many coatings (e. g. primers, without inorganic gellants), glues, many shampoos
The terms shear-thinning and pseudoplastic are identical in their meaning (see also Chapter 14.3: 1925, with the concepts of Eugen C. Bingham [3.4], Wolfgang Ostwald jun. [3.2] [3.3] – the latter used the German term “strukturviskos” – and others on this subject [3.5]). However, pseudoplastic contains the word plastic, a behavior which cannot be exactly determined in a scientific sense since it is the result of inhomogeneous deformation and flow behavior (see also Chapter 3.3.4.2c and Figure 2.9: no. 4). This is the reason why the use of the term “pseudoplastic” is diminishing more and more in current literature.
Note: Apparent shear viscosity
Often the term “apparent viscosity” is used with different meanings about the measured viscosity values. Therefore, actually this term should be avoided as it is superfluous [3.33] [3.78].
Meaning 1: Related to rheology it means that a sample does not show ideal-viscous flow behavior. If the ratio of shear stress to shear rate varies with the shear load, the corresponding values are often called the “apparent shear viscosity” at the corresponding shear rate, to illustrate that these kinds of values are different from constant viscosity values of ideal-viscous fluids (according to ASTM D4092). Each one of these viscosity values obtained represents a single point of the viscosity function only. Therefore, these viscosity values can only be evaluated in the appropriate form if information is also given about the shear conditions. Examples for accurate specifications are as follows:
η( γ ̇ = 100 s-1) = 345 mPas, or η(τ = 500 Pa) = 12.5 Pas